Textile grade CMC Sodium carboxymethyl cellulose is used in textile industry as sizing agent, thickening agent of printing and dyeing pulp, textile printing and stiffening finishing. Used in sizing agent can improve solubility and viscosity, and easy desizing; As a stiffening finishing agent, its dosage is more than 95%; When used as sizing agent, the strength and flexibability of sizing film are improved obviously. The results show that when the concentration of CMC solution is about 1%(W/V), the chromatographic performance of the prepared thin layer plate is better. At the same time, the thin layer plate coated under the optimized conditions has appropriate layer strength, which is suitable for various sample adding technologies and convenient for operation. CMC has adhesion to most fibers and can improve the bond between fibers. Its stable viscosity ensures the uniformity of sizing, thus improving the efficiency of weaving. Can also be used in textile finishing agent, especially anti-wrinkle finishing, to bring durability changes.
Textile grade CMC can improve the yield and strength in textile spinning process. Used for textile printing and dyeing, as a suspending agent of raw materials, improve bond rate and printing quality, recommended for spinning 0.3-1.5%, 0.5-2.0% for printing and dyeing.
Typical properties
Appearance | White to off-white powder |
Particle size | 95% pass 80 mesh |
Degree of substitution | 1.0-1.5 |
PH value | 6.0~8.5 |
Purity (%) | 97min |
Popular grades
Application | Typical grade | Viscosity (Brookfield, LV, 2%Solu) | Viscosity (Brookfield LV, mPa.s, 1%Solu) | Degree of Substitution | Purity |
CMC for textile and dyeing | CMC TD5000 | 5000-6000 | 1.0-1.5 | 97%min | |
CMC TD6000 | 6000-7000 | 1.0-1.5 | 97%min | ||
CMC TD7000 | 7000-7500 | 1.0-1.5 | 97%min |
Textile grade CMC Sodium carboxymethyl cellulose is used in textile industry as sizing agent, thickening agent of printing and dyeing pulp, textile printing and stiffening finishing. Used in sizing agent can improve solubility and viscosity, and easy desizing; As a stiffening finishing agent, its dosage is more than 95%; When used as sizing agent, the strength and flexibability of sizing film are improved obviously. The results show that when the concentration of CMC solution is about 1%(W/V), the chromatographic performance of the prepared thin layer plate is better. At the same time, the thin layer plate coated under the optimized conditions has appropriate layer strength, which is suitable for various sample adding technologies and convenient for operation. CMC has adhesion to most fibers and can improve the bond between fibers. Its stable viscosity ensures the uniformity of sizing, thus improving the efficiency of weaving. Can also be used in textile finishing agent, especially anti-wrinkle finishing, to bring durability changes.
Textile grade CMC can improve the yield and strength in textile spinning process. Used for textile printing and dyeing, as a suspending agent of raw materials, improve bond rate and printing quality, recommended for spinning 0.3-1.5%, 0.5-2.0% for printing and dyeing.
Typical properties
Appearance | White to off-white powder |
Particle size | 95% pass 80 mesh |
Degree of substitution | 1.0-1.5 |
PH value | 6.0~8.5 |
Purity (%) | 97min |
Popular grades
Application | Typical grade | Viscosity (Brookfield, LV, 2%Solu) | Viscosity (Brookfield LV, mPa.s, 1%Solu) | Degree of Substitution | Purity |
CMC for textile and dyeing | CMC TD5000 | 5000-6000 | 1.0-1.5 | 97%min | |
CMC TD6000 | 6000-7000 | 1.0-1.5 | 97%min | ||
CMC TD7000 | 7000-7500 | 1.0-1.5 | 97%min |